FIBER BLENDED: 100% META ARAMID
DINER: 200D, 600D, 840D, 1000D, 1500D,3000D
COLOR:  RAW WHITE, DOPE DYED

High Strength and High Modulus 

Due to the high hydrogen bonds, the strength of Taparan®para aramid can reach up to above 28g/D.Its specific strength is 5-6 times that of steel wire , its specific modulus is 2-3 times that of steel wire or glass fiber , and its flexibility is 2 times that of steel wire while the weight is only 1/5 that of the steel wire.

Excellent Flame resistant

The limiting oxygen index(LOI) is over 29%. start to carbonise and decompose above 530℃

High temperature resistant

Can be used continuously in a very wide temperature range from -196℃ to 204℃.It has no decomposing or melting at 500℃.Its tenacity remains 75% after 100hours under 200℃.

Good Chemical Resistance

Para aramid is acid and alkali resistant, anti-aging with good adhesive force in rubber;

High temperature resistant

Can be used continuously in a very wide temperature range from -196℃ to 204℃.It has no decomposing or melting at 500℃.Its tenacity remains 75% after 100hours under 200℃.

Good textile properties

High resistance to breakage and its high break elongation ratio guaranteed the end product with high intensity, good product longevity, and better tolerance to injection;

No Melt Drip properties

It is flame resistant with self-extinguish nature and non-melt drip characteristic.